桥梁缆索高强钢丝均匀腐蚀及点蚀的规律
Experiment Research on Uniform Corrosion and Pitting Corrosion of High-Strength BridgeWires
投稿时间:2018-01-04  修订日期:2018-03-12
DOI:10.11908/j.issn.0253-374x.2018.12.001     稿件编号:    中图分类号:U443.38
 
摘要点击次数: 83    全文下载次数: 55
中文摘要
      为了研究桥梁缆索高强钢丝均匀腐蚀及点蚀的规律,采用酸性盐雾试验制作了6种共30根不同腐蚀程度的钢丝试件,通过质量分析、三维扫描等手段,研究了腐蚀高强钢丝均匀腐蚀深度、点蚀深度的演变规律.试验结果表明:均匀腐蚀深度随腐蚀时长的变化遵循幂函数规律,均匀腐蚀深度的变异系数随腐蚀时长减小;钢丝的点蚀深度服从正态分布,最大点蚀深度服从极值I型分布.最后,建立了均匀腐蚀深度与最大点蚀深度的预测模型,并运用于具体实桥分析预测中.
英文摘要
      In order to study the uniform corrosion and pitting corrosion of high strength bridge wires, a total of 30 steel wire specimens on six corrosion levels were prepared by using the acetic acid salt spray test. The variation of uniform corrosion depth and pitting depth was evaluated by using weight analysis and three dimension scanning. The results show that the measured uniform corrosion depth follows the power law distribution. The coefficient of variation of uniform corrosion depth decrease with the corrosion time. The pitting depth follows the normal distribution and maximum pitting depth follows the extreme value distribution. Finally, the prediction models for uniform corrosion depth and maximum pitting depth were established and then applied to the real cables on the bridge.
HTML   查看全文  查看/发表评论  

您是第4905306位访问者
版权所有《同济大学学报(自然科学版)》
主管单位:教育部 主办单位:同济大学
地  址: 上海市四平路1239号 邮编:200092 电话:021-65982344 E-mail: zrxb@tongji.edu.cn
本系统由北京勤云科技发展有限公司设计